Monitoramento da biodeterioração da madeira de três espécies amazônicas pela técnica da colorimetria / Monitoring of biodeterioration of three Amazonian wood species by the colorimetry technique

This work aimed to evaluate the use of colorimetry in the characterization of biodeterioration marupá, jequitibá and cumaru wood, submitted to white and brown rot. For this purpose, specimens of each Amazonian species were submitted to accelerated decay tests, according to American Society for Testing and Materials - ASTM D2017, during 20 weeks. With a colorimeter, the colorimetric parameters L* (lightness), a* (green-red coordinate), b* (blue-yellow coordinate) and total color change (ΔE) were determined weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss. The results indicated that the colorimetry was effective in monitoring of biodeterioration of wood, as well as to differentiate white and brown rot. The best predictions of natural resistance to white and brown rot were obtained with the parameters b* and L*, respectively. We also emphasizes the use of ΔE to estimate the biodeterioration of wood, because of their significant correlations with weight loss.

Objetivou-se avaliar o emprego da colorimetria na caracterização da biodeterioração das madeiras de marupá, jequitibá e cumaru submetidas ao ataque de fungos de podridão branca e parda. Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a American Society for Testing and Materials - ASTM D2017, durante 20 semanas. Os parâmetros colorimétricos L* (luminosidade), a* (coordenada verde-vermelho), b* (coordenada amarelo-azul) e a variação total da cor (ΔE) foram determinados semanalmente até a quarta semana, e posteriormente a cada duas semanas até a vigésima semana, com auxílio de um espectrofotocolorímetro. Adicionalmente, foram determinadas as perdas de massa dos corpos de prova. Os resultados permitiram destacar que a colorimetria foi eficaz no monitoramento da biodeterioração da madeira, bem como para diferenciação da podridão branca e parda. As melhores predições da resistência natural aos fungos de podridão branca e parda foram obtidas com os parâmetros b* e L*, respectivamente. Enfatiza-se também, o emprego da ΔE como parâmetro auxiliar na estimativa da biodeterioração da madeira, em razão de suas correlações significativas com a perda de massa.

Dureza Rockwell da madeira de três espécies amazônicas submetidas a ensaios de apodrecimento acelerado / Rockwell hardness of the wood of three Amazon species submitted to decay accelerated tests

Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.

This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.

Durabilidade natural de painéis aglomerados confeccionados com Eucalyptus grandis e Bambusa vulgaris em ensaio de apodrecimento acelerado / Natural durability of Eucalyptus grandis and Bambusa vulgaris particleboards under accelerated fungi decay test

O conhecimento acerca da resistência dos compostos ligno-celulósicos ao ataque de microrganismos é primordial para servir de base à prevenção da deterioração e a correta destinação de emprego do material. Nesse sentido, avaliou-se a resistência natural a fungos apodrecedores de painéis aglomerados confeccionados com partículas de madeira (Eucalyptus grandis) e/ou bambu (Bambusa vulgaris). Foram produzidas, em laboratório, chapas aglomeradas nas dimensões 50x50x0,95cm e massa específica pré-estabelecida em 0,70g cm-3, nas proporções de 100:0, 75:25, 50:50, 25:75 e 0:100 de madeira e bambu, respectivamente. A massa de partículas representou 91 por cento da massa seca de cada painel, sendo, o restante, formado pelo adesivo ureia-formaldeído (8 por cento) e parafina (1 por cento). Para determinação da resistência natural ao ataque de fungos xilófagos, os painéis foram testados em laboratório e utilizados os fungos Gloeophyllum trabeum (podridão parda) e Trametes versicolor (podridão branca), de acordo com a ASTM D 2017 (2005). Quanto aos resultados, foi observado que os painéis confeccionados com mistura de partículas de madeira e bambu apresentaram menor resistência ao ataque dos fungos apodrecedores. Painéis que utilizaram apenas bambu ou madeira apresentaram resistência biológica semelhante. Dentre os fungos, T. versicolor atacou mais severamente os painéis.

The knowledge about lignocellulosic compounds strength to the attack of microorganisms is essential for preventing deterioration and also for knowing the correct usage of the material. Accordingly it was evaluated the natural resistance of wood panels made of particles of wood (Eucalyptus grandis) and/or bamboo (Bambusa vulgaris) to decay fungi. Particleboards were produced in laboratory, each of them with dimensions 50x50x0.95cm and density pre-set at 0.70g cm-3, in proportions of 100:0, 75:25, 50:50, 25:75 and 0:100 of wood and bamboo, respectively. The particles mass represented 91 percent of the dry mass of each panel while the remainder was formed by the urea-formaldehyde adhesive (8 percent) and paraffin (1 percent). The panels were tested in the laboratory and Gloeophyllum trabeum (brown rot) and Trametes versicolor (white rot) were used to determine the natural resistance to attack by wood decay fungi. It was observed that panels which were made with a mixture of particles of wood and bamboo were less resistant to attack by decay fungi. Panels that were made from bamboo or wood only showed similar biological resistance. Among fungi, T. versicolor was the one that attacked panels more severely.